SO42−–Mn–Co–Ce supported on TiO2/SiO2 with high sulfur durability for low-temperature SCR of NO with NH3
•Excellent SO2 durability at low temperature is obtained with SO42 − MnCoCe/T/S.•The catalyst exhibits best NOx conversion efficiency of 99.5% at 250 °C.•The NOx conversion does not decrease after repeatedly used for 8 times.•Sulfating and T/S support increase surface area and decrease crystallinity.
The catalysts SO42 − Mn–Co–Ce/TiO2/SiO2 were investigated for the low-temperature SCR of NO with NH3 in the presence of SO2. An excellent SO2 durability at low temperature was obtained with the catalyst used TiO2/SiO2 as support and modified with SO42 −. The catalyst sulfated with 0.1 mol/L H2SO4 solution and then calcined at 300 °C exhibited the best NOx conversion efficiency of 99.5% at 250 °C in the presence of 50 ppm SO2. The conversion efficiency did not decrease after repeatedly used for 8 times.
Graphical abstractFigure optionsDownload full-size imageDownload as PowerPoint slide
Journal: Catalysis Communications - Volume 78, 10 March 2016, Pages 22–25