Title
NOx storage and reduction pathways on zirconia and titania functionalized binary and ternary oxides as NOx storage and reduction (NSR) systems
Abstract

•Alumina acts as a diffusion barrier in AZT preventing formation of ZrTiO4.•AZT ternary oxide has a higher SSA and NSC than that of ZT binary oxide.•Adsorbed NOx species are thermally more stable on AZT ternary oxide.•Pt addition increases NSC and decreases nitrate reduction temperature.

Binary and ternary oxide materials, ZrO2/TiO2 (ZT) and Al2O3/ZrO2/TiO2 (AZT), as well as their Pt-functionalized counterparts were synthesized and characterized via XRD, Raman spectroscopy, BET, in situ FTIR and TPD techniques. In the ZT system, a strong interaction between TiO2 and ZrO2 domains at high temperatures (>973 K) resulted in the formation of a low specific surface area (i.e. 26 m2/g at 973 K) ZT material containing a highly ordered crystalline ZrTiO4 phase. Incorporation of Al2O3 in the AZT structure renders the material highly resilient toward crystallization and ordering. Alumina acts as a diffusion barrier in the AZT structure, preventing the formation of ZrTiO4 and leading to a high specific surface area (i.e. 264 m2/g at 973 K). NOx adsorption on the AZT system was found to be significantly greater than that of ZT, due to almost ten-fold greater SSA of the former surface. While Pt incorporation did not alter the type of the adsorbed nitrate species, it significantly boosted the NOx adsorption on both Pt/ZT and Pt/AZT systems. Thermal stability of nitrates was higher on the AZT compared to ZT, most likely due to the defective structure and the presence of coordinatively unsaturated sites on the former surface. Pt sites also facilitate the decomposition of nitrates in the absence of an external reducing agent by shifting the decomposition temperatures to lower values. Presence of Pt also enhances partial/complete NOx reduction in the absence of an external reducing agent and the formation of N2 and N2O. In the presence of H2(g), reduction of surface nitrates was completed at 623 K on ZT, while this was achieved at 723 K for AZT. Nitrate reduction over Pt/ZT and Pt/AZT via H2(g) under mild conditions initially leads to conversion of bridging nitrates into monodentate nitrates/nitrites and the formation of surface OH and NHx functionalities. N2O(g) was also continuously generated during the reduction process as an intermediate/byproduct.

Graphical abstractFigure optionsDownload full-size imageDownload high-quality image (173 K)Download as PowerPoint slide

Keywords
Zirconia; Titania; Pt; NOx; LNT; NSR
First Page Preview
NOx storage and reduction pathways on zirconia and titania functionalized binary and ternary oxides as NOx storage and reduction (NSR) systems
Get Full-Text Now
Don't Miss Today's Special Offer
Price was $35.95
You save - $31
Price after discount Only $4.95
100% Money Back Guarantee
Full-text PDF Download
Online Support
Any Questions? feel free to contact us
Publisher
Database: Elsevier - ScienceDirect
Journal: Catalysis Today - Volume 231, 1 August 2014, Pages 135–144
Authors
, , ,
Subjects
Physical Sciences and Engineering Chemical Engineering Catalysis
Get Full-Text Now
Don't Miss Today's Special Offer
Price was $35.95
You save - $31
Price after discount Only $4.95
100% Money Back Guarantee
Full-text PDF Download
Online Support
Any Questions? feel free to contact us